PETG-GF Pellet
- PETG pellets with 10% glass fiber
- Enhanced clarity and rigidity
- Chemical resistance and dimensional stability
Request a custom quote for your required quantities and secure the best conditions.
PETG-GF pellets for 3D printing contain 10% glass fiber, offering a unique combination of clarity and rigidity. The material is known for its high chemical resistance, dimensional stability, and easy processing, making it ideal for industrial applications requiring strong and aesthetic parts. PETG-GF is the right choice for medium-scale prototyping and components that must combine durability with a professional finish.
Technical Datasheet — PETG-GF Pellet
Physical Properties
| Property | Test Method | Typical Value |
|---|---|---|
| Density (21.5 °C) | ASTM D792 (ISO 1183, GB/T 1033) | 1.30 g/cm³ |
| Melt Index (230 °C / 2.16 kg) | ASTM D1238 | 20-24 g/10 min |
| Glass Transition Temperature (Tg) | DSC, 10 °C/min | 70 °C |
| Vicat Softening Temperature | ASTM D1525 (ISO 306, GB/T 1633) | 80 °C |
| Heat Deflection Temperature (HDT) 1.8 MPa | ISO 75 | 63 °C |
| Heat Deflection Temperature (HDT) 0.45 MPa | ISO 75 | 69 °C |
Mechanical Properties
General Values
| Property | Test Method | Typical Value |
|---|---|---|
| Young’s Modulus | ASTM D638 (ISO 527, GB/T 1040) | 3257 ± 16 MPa |
| Tensile Strength | ASTM D638 (ISO 527, GB/T 1040) | 68.1 ± 0.6 MPa |
| Elongation at Break | ASTM D638 (ISO 527, GB/T 1040) | 3.0 ± 0.04 % |
| Bending Modulus | ASTM D790 (ISO 178, GB/T 9341) | 3932 ± 9 MPa |
| Bending Strength | ASTM D790 (ISO 178, GB/T 9341) | 107.2 ± 0.4 MPa |
| Charpy Impact Strength | ASTM D256 (ISO 179, GB/T 1043) | 3.6 ± 0.3 kJ/m² |
X-Y / Z Directions
| Property | Direction / Test Method | Typical Value |
|---|---|---|
| Young’s Modulus (X-Y) | ASTM D638 (ISO 527, GB/T 1040) | 3288 ± 85 MPa |
| Tensile Strength (X-Y) | ASTM D638 (ISO 527, GB/T 1040) | 68.1 ± 0.8 MPa |
| Elongation at Break (X-Y) | ASTM D638 (ISO 527, GB/T 1040) | 3.5 ± 0.42 % |
| Bending Modulus (X-Y) | ASTM D790 (ISO 178, GB/T 9341) | 3332 ± 69 MPa |
| Bending Strength (X-Y) | ASTM D790 (ISO 178, GB/T 9341) | 93.2 ± 2.7 MPa |
| Charpy Impact Strength (X-Y) | ASTM D256 (ISO 179, GB/T 1043) | 4.5 ± 0.3 kJ/m² |
| Young’s Modulus (Z) | ASTM D638 (ISO 527, GB/T 1040) | 2551 ± 87 MPa |
| Tensile Strength (Z) | ASTM D638 (ISO 527, GB/T 1040) | 43.4 ± 0.3 MPa |
| Elongation at Break (Z) | ASTM D638 (ISO 527, GB/T 1040) | 2.6 ± 0.17 % |
| Bending Modulus (Z) | ASTM D790 (ISO 178, GB/T 9341) | 2292 ± 141 MPa |
| Bending Strength (Z) | ASTM D790 (ISO 178, GB/T 9341) | 60.6 ± 3.4 MPa |
| Charpy Impact Strength (Z) | ASTM D256 (ISO 179, GB/T 1043) | 6.6 ± 0.8 kJ/m² |
Recommended Printing Conditions
| Parameter | Setting |
|---|---|
| Drying Temperature | 50-55 °C |
| Drying Time | 4-8 hours |
| Maximum Moisture Content | 0.5 % |
| Barrel Zone 1 Temperature | 170-200 °C |
| Barrel Zone 2 Temperature | 220-240 °C |
| Barrel Zone 3 Temperature | 220-240 °C |
| Nozzle Temperature | 220-230 °C |
| Bed Temperature | Room temperature - 70 °C |
3305050006
You might also like
Comments (0)
No customer reviews for the moment.
- PETG pellets with 10% glass fiber
- Enhanced clarity and rigidity
- Chemical resistance and dimensional stability
Request a custom quote for your required quantities and secure the best conditions.